QQ BEF-PTB-950S
| Item No.: | PTB-950S |
Supplier Details
Country: Taiwan
City: New Taipei City
Address: 7F., NO.3, GUIFENG ST., TAISHAN DIST., NEW TAIPEI CITY 24355, TAIWAN (R.O.C.)
TEL: +886-2-29010509
Fax: +886-2-29014616
Online Showroom:
68 Products
■ Product Features
1. Excellent optical properties after UV molding.
2. After curing the surface of low yield, low warpage of the substrate.
3. Has the strength and toughness, pulling prone to breaking.
■ Resin Specifications
1.Chemical Composition: Acrylic resin
2.Physical Status: Fluid @ 25 ℃
3.Appearance: Clear yellow
4.Solid content: approach 100%
5.Liquid refractive index: 1.584 ± 0.005
6.Resin gravity: 1.11 g / cm3
■ Hardening conditions
1. The resin-coated at a thickness of 25μm, it is recommended UV accumulated energy greater than 300 mj / cm2.
2. It is recommended to use a solvent-free process.
3. Recommends wheel with operating temperature: 45 ~ 50 ℃, the production rate: less than 10M / min.
■ Finished properties (Sunbeam C87H 125 μm PET)
1.Coating thickness: 25 mm (dry film thickness)
2.Refractive index (RI) at a wavelength of 633nm: 1.602
3.Haze: less than 1.0%
4.Pencil Hardness (weight 765g): F
5.100 grid knives (after molding): 5B
6.100 grid knives (ring measured after 500 hours **): 5B
1. Excellent optical properties after UV molding.
2. After curing the surface of low yield, low warpage of the substrate.
3. Has the strength and toughness, pulling prone to breaking.
■ Resin Specifications
1.Chemical Composition: Acrylic resin
2.Physical Status: Fluid @ 25 ℃
3.Appearance: Clear yellow
4.Solid content: approach 100%
5.Liquid refractive index: 1.584 ± 0.005
6.Resin gravity: 1.11 g / cm3
■ Hardening conditions
1. The resin-coated at a thickness of 25μm, it is recommended UV accumulated energy greater than 300 mj / cm2.
2. It is recommended to use a solvent-free process.
3. Recommends wheel with operating temperature: 45 ~ 50 ℃, the production rate: less than 10M / min.
■ Finished properties (Sunbeam C87H 125 μm PET)
1.Coating thickness: 25 mm (dry film thickness)
2.Refractive index (RI) at a wavelength of 633nm: 1.602
3.Haze: less than 1.0%
4.Pencil Hardness (weight 765g): F
5.100 grid knives (after molding): 5B
6.100 grid knives (ring measured after 500 hours **): 5B